Axial Leaded Glass Encapsulated Diode DO35 Shape NTC Thermistor Temperature Sensor, 200K Ohm, Beta B(25/50): 3899K, Operating Temperature Range -40C to +250C.
Unit: mm
- NTC Thermistor chip hermetically sealed in DO35 glass shell.
- Tinned Dumet wire
Axial lead glass encapsulated NTC thermistor used for high temperature measurement, sensing, monitoring, detection and control. Typical application such as industrial process control, HVAC, oven, office equipment, etc.
- Resistance at 25C R25: 200K ohm+/-2%
- Beta Value B(25/50): 3899K+/-1%
- Optional R25 resistance tolerance, ±1%(F), ±2%(G), ±3%(H), or ±5%(J)
- Dissipation Factor: δ≥2mW/℃
- Thermal Time Constant (in still air): 12 seconds max.
- Rated Power: ≤50mW
- Insulation resistance: room temperature, 50VDC, 60 Seconds, ≥100MΩ.
- Operating temperature range: -40 to +250C.
| Temperature Centigrade |
Resistance (K Ohm) |
Temperature Centigrade |
Resistance (K Ohm ) |
Temperature Centigrade |
Resistance (K Ohm) |
|---|---|---|---|---|---|
| -40C | 5904.6812 KΩ | 80C | 27.5128 KΩ | 200C | 1.2687 KΩ |
| -35C | 4348.6465 KΩ | 85C | 22.0580 KΩ | 205C | 1.1556 KΩ |
| -30C | 3144.8796 KΩ | 90C | 18.8536 KΩ | 210C | 1.0553 KΩ |
| -25C | 2320.0264 KΩ | 95C | 16.1746 KΩ | 215C | 0.9662 KΩ |
| -20C | 1760.4601 KΩ | 100C | 13.9264 KΩ | 220C | 0.8868 KΩ |
| -15C | 1367.0424 KΩ | 105C | 12.0329 KΩ | 225C | 0.8159 KΩ |
| -10C | 1076.2418 KΩ | 110C | 10.4325 KΩ | 230C | 0.7524 KΩ |
| -5C | 851.5250 KΩ | 115C | 9.0752 KΩ | 235C | 0.6955 KΩ |
| 0C | 672.9399 KΩ | 120C | 7.9200 KΩ | 240C | 0.6443 KΩ |
| 5C | 529.6061 KΩ | 125C | 6.9337 KΩ | 245C | 0.5982 KΩ |
| 10C | 415.0318 KΩ | 130C | 6.0889 KΩ | 250C | 0.5566 KΩ |
| 15C | 324.5364 KΩ | 135C | 5.3629 KΩ | ||
| 20C | 254.0953 KΩ | 140C | 4.7372 KΩ | ||
| 25C | 200.0000 KΩ | 145C | 4.1963 KΩ | ||
| 30C | 158.8782KΩ | 150C | 3.7274 KΩ | ||
| 35C | 127.7940 KΩ | 155C | 3.3196 KΩ | ||
| 40C | 104.3055 KΩ | 160C | 2.9641 KΩ | ||
| 45C | 86.4564 KΩ | 165C | 2.6382 KΩ | ||
| 50C | 72.7196 KΩ | 170C | 2.3553 KΩ | ||
| 55C | 61.9211 KΩ | 175C | 2.1092 KΩ | ||
| 60C | 53.1649 KΩ | 180C | 1.8945 KΩ | ||
| 65C | 45.7722 KΩ | 185C | 1.7065 KΩ | ||
| 70C | 39.2403 KΩ | 190C | 1.5417 KΩ | ||
| 75C | 33.2210 KΩ | 195C | 1.3966 KΩ |
| Test | Standard | Test Conditions and methods | Requirements |
|---|---|---|---|
| Soldering & Solderability | IEC60068-2-20 Test Ta |
Temperature: 230±5 ℃， 2-2.5mm away from ceramic body On: 2±0.5 Seconds. |
The terminations shall be evenly tinned |
| Resistant to soldering heat | IEC60068-2-20 Test Tb |
Temperature: 260±5℃, 2-2.5mm away from ceramic body On：10±1 Seconds. |
No visible damage, ΔR25/R25≤3% |
| Lead wire tensile | IEC60068-2-21 Test U |
Test Ua: Force 10N, On 10 Seconds; Test Ub: Bending 90C, Force 5N, Twice. |
No break off, ΔR25/R25≤3% |
| Test | Standard | Test Conditions | ΔR25/R25 (typical) | Remarks |
|---|---|---|---|---|
| Low temperature storage | IEC 60068-2-1 | Storage at low category temperature: -30 oC, Time: 1000 hours |
≤3% | No visible damage |
| Storage in dry heat | IEC 60068-2-2 | Storage at upper category temperature: 200 oC, Time: 1000 hours |
≤3% | No visible damage |
| Storage in damp heat, steady state (Humidity test) | IEC 60068-2-3 | Temperature: 40oC, Humidity:90%-95% RH, Duration:1000 hours |
≤3% | No visible damage |
| Temperature cycling | IEC 60068-2-14 | 1. -30C/30 minutes 2. 80C/5 minutes 3. 200C/30 minutes 4. 80C/5 minutes. Number of cycles: 5 Cycles |
≤3% | No visible damage |
Minimum lead wire length tailored to shall be ≥8mm.
In lead wire bending, bending point shall be more than 2mm away from glass body part.
Mounting and Handling Recommendations
Excessive forces applied to a sensor may cause serious damage. To avoid this, the following recommendations should be adhered to:
- No perpendicular forces must be applied to the body
- During bending, the leads must be supported
- Bending close to the body must be done very carefully
- Axial forces to the body can influence the accuracy of the sensor and should be avoided
- These sensors can be mounted on a minimum pitch of >5 mm
Soldering and Welding
- Avoid any force on the body or leads during, or just after, soldering.
- Do not correct the position of an already soldered sensor by pushing, pulling or twisting the body.
- Prevent fast cooling after soldering.
- For hand soldering, where mounting is not on a printed-circuit board, the soldering temperature should be <300C the soldering time <3 s and the distance between body and soldering point >1.5 mm.
- For hand soldering, dip, wave or other bath soldering, mounted on a printed-circuit board, the
- soldering temperature should be <300C, the soldering time <5 s and the distance between body and soldering point >1.5 mm.
- The distance between the body and the welding point should be >0.5 mm. Care should be taken to ensure that welding current never passes through the sensor.
Other Related AMWEI NTC Thermistors Products for Temperature Sensing
Content Headline
Technical Knowledge
NTC Thermistor Glossary and Definition
How NTC thermistor beta value is calculated?
NTC Thermistor Manufacturing Process and Quality Control
Applications Articles
How to Select NTC Thermistor for Inrush Current Limiting?
NTC thermistor for temperature measurement and control selecting reference information.
Charging Control with AMWEI NTC thermistor
Reliable limiting of current surges by AMWEI NTC and PTC thermistor
How to Select Packaged Thermistor Temperature Sensor Probe Assembly ? 6 Steps